  • PLATING RESIST MR-303F油墨

    PLATING RESIST MR-303F是适合用于部分镀金用的遮蔽的单液性, 碱性剥离型抗镀油墨.此外也适合用于ITO用的蚀刻油墨.

     
    PLATING RESIST MR-303F is one component, alkaline removable type Resist Ink developed for masking of partial Au plating.
    Moreover, it is possible to be used as etching ink for ITO.

    Main Feature
    1. Cured film has flexibility, and available for a flexible board and a rigid board.
    2. This ink has excellent resistance to Au plating( Electro-less),since the contamination to the plating solution
    is very small, control of the solution is easy.
    3. Possible to be used as etching ink for ITO.

    Main Property

    Items
    Representing value
    Remarks
    Color
    Black color
    Visual
    Viscosity at 25 deg.C
    200 dPa・s
    Viscotester VT-04
    Applicable Screen
    150~250 Mesh
    Polyester Screen
    Optimum Ink thickness after drying
    10~20µm
    Thickness Meter
    Dry Conditions
    100deg.C × 10min
    Circulating Heat Oven
    Adhesion
    100 / 100
    Cross-cut,tape peel test
    Resistance to Electro-less Plating
    No penetration, No color change
    Ni Plating at 90deg.C for 30 min + Au Plating at 90deg.C for 40 min
    Remove of the cured film
    1~3 wt% NaOH Solution
    30deg.C × 1~3 min Dipping

    The above information obtained by actual measurement at our lab., and do not specified values.
    < Shelf-life > Main body: 6 months --- Stored in 25 deg.C or below (cool and dark place).
    Usage and handling precautions
    1. If dilution is needed due to viscosity variation during operation, dilute with exclusive reducer #70 within 5%.
    2. Drying should be done at the range of 100deg.C~130deg.C. Since drying time will vary based on s heat efficiency and ventilation capacity of used oven, please confirm your oven and set optimum condition.
    3. This resist can be used for general Ni/Au plating solution without any inconvenience.

    However, if it is used for special plating solution, it may cause the change in characteristics, depending on its composition. Please use it after checking fully.

    Flexibility test (JIS K 5600-5-1)

    Mandrel diameter
    8mmφ
    6mmφ
    4mmφ
    3mmφ
    2mmφ
    Conventional products
    No Crack
    Crack
    Crack
    Crack
    Crack
    MR-303F
    No Crack
    No Crack
    No Crack
    No Crack
    No Crack

    Test board: Thickness 25µm/PI film
    Screen mesh: 200mesh polyester screen
    Dry condition: 100deg.C × 10min Circulating Heat Oven
    Ink thickness after drying: Thickness 14~16µm

    Elusion amount in Electro-less Ni Plating 

     

     ・Absorbance is high=Quantity of elution is large ・Absorbance is low=Quantity of elution is small Compared to Ni Plating new solution, absorbance peak which arise from elusion content from coated film can be confirmed at around 280nm for conventional product though, the peak can not be confirmed in MR-303F.

    <<Sample manufacture condition>>
    Test Board: 5.6cm×4cm /PI film/4 pieces
    Dry condition: 100deg.C × 10min Circulating Heat Oven
    Ink thickness after drying: About 30µm
    <<Ni plating condition>>
    Plating solution: Product made by OKUNO CHEMICAL INDUSTRIES CO.,LTD
    Dip condition: 80 deg.C × 4hr
    <<Measurement condition>>
    Testing equipment: Product made in SHIMADZU CORPORATION UV-1800
    Kind of measurements: Absorbance
    Measurement wavelength(nm): 200~900

    ITO-proof etching liquid test 

    <<Sample manufacture condition>>
    Test Board: ITO/PET film
    Screen mesh: 200mesh polyester screen
    Dry condition: 100deg.C × 10min Circulating Heat Oven
    Ink thickness after drying: Thickness 10~15µm

    ≪ITO etching liquid condition≫
    Etching solution: Mixed acid ITO-02 Product made by KANTO CHEMICAL CO.,INC.
    Dip condition: 45deg.C × 4min
     ≪Remove of the cured film≫
    Remove solution: 3wt%NaOH
    Dip condition: 30 deg.C × 1min
    ≪Measuring instrument condition≫
    Measuring instrument Product made by YOKOGAWA ELECTRIC CORPORATION DEGITAL MLTIMETER 755S

    Stripping test after thermal resistance 


    <<Sample manufacture condition>>
    Test Board: PI film・ Glass epoxy copper foil
    Screen mesh: 200mesh polyester screen
    Dry condition: 100deg.C × 10min Circulating Heat Oven
    Ink thickness after drying: Thickness 10~15µm
    Additional heating condition: 180℃×1-5hr/ Heat circulation oven
    ≪Remove of the cured film≫
    Remove solution: 3wt%NaOH
    Dip condition: 30 deg.C × 1min
    Check strippability: Visual

     

  • CST (Asia) Limited  电话: 深圳: 0755-2308 6405 苏州: 0512-52821513 香港: 00852-2602-6173
    地址:香港新界沙田火炭穗禾路1号丰利工业中心4字楼13室  在线QQ:  893008608
    Copyright(C) 51Touch.Com All rights reserved   技术支持:乐虎国际官网登录与OLED网   电话:13183843395
    名站导航: 乐虎国际官网登录与OLED网 | 乐虎国际官网登录B2B | 乐虎国际官网登录论坛 | 乐虎国际官网登录人才 | 乐虎国际官网登录杂志


    客服: